PEMANFAATAN LIMBAH FLY ASH DAN BOTTOM ASH DARI PLTU SUMSEL-5 SEBAGAI BAHAN UTAMA PEMBUATAN PAVING BLOCK

Hadi Winarno, Damris Muhammad, Yudha Gusti Wibowo

Sari


Fly ash and bottom ash are solid waste from coal combustion in the operating system of Steam Power Plant (PLTU). The research was conducted by combining fly ash and bottom ash with an adhesive consisting of portland cement. Based on the tests performed the maximum mixture obtained with cement samples, fly ash and bottom ash is 1: 2: 2. Paving blocks made from fly ash and bottom ash have compressive strength values resulting in compressive strength values of 50.52 MPa. This value indicates that the sample is in the class of paving blocks A. Paving Block made from fly ash and bottom ash also has a very good average air absorption value, in a combination of suitable cement mixtures, fly ash and bottom ash (1: 2: 2) the average air absorption value is still 5.06%. This value shows that the sample is in class B paving blocks.


Kata Kunci


Fly Ash, Bottom Ash, Cement, Paving Block

Teks Lengkap:

PDF

Referensi


Akbar, Muhammad 2009, Kinerja Econimizer pada Boiler. Surabaya : Institut Teknologi Sepuluh November.

Bangunan, P.T.K., 2002. Tata Cara Perencanaan Struktur Beton Untuk Bangunan Gedung SNI 03-2847-2002.

China National Electrical Engineering, 2013. Mine Mouth CFSPP SUMSEL-5 (2x150MW) Vol.6. Ash Handling. China National Electrical Engineering. Co. Ltd.

China National Electric Engineering Company. 2014. Mine Mouth CFSPP SUMSEL-5 : Beijing.

Dyahwanti, Inarni Nur. 2007. Kajian Dampak Lingkungan Kegiatan Penambangan Pasir pada Daerah Sabuk Hijau Gunung Sumbing Daerah Kabupaten Tumanggung. ITS. Surabaya.

Eunike, Filia S P . 2014 . Kuat Tarik Lentur Beton Geopolymer berbasis Abu Terbang (Fly Ash). Universitas Sam Ratulangi. Manado

Faridah, A.M, 2012. Karakteristik Abu Dasar PLTU Paiton: Pengaruh Perlakuan Magnet , HCl dan Fusi dengan NaOH. Pusat Studi Energi, ITS. Surabaya.

Harris, H., Anam, S., & Mahmudsyah, S, 2013. Studi pemanfaatan limbah padat dari perkebunan kelapa sawit pada PLTU 6 MW di Bangka Belitung. Jurnal Teknik ITS, Surabaya.

Ismunandar, 2006, Padatan Oksida Logam :Struktur, Sintesis, dan Sifat-sifatnya. ITB, Bandung.

Kemas AH. 1995. Rancangan Percobaan Teori dan Aplikasi. Raja Grafindo Persada, Jakarta

Kurniawan, F. 2008. Implementasi Sistem Dinamik pada Pengembangan Pola Kemitraan Industri Kecil Dan Menengah Di Dki Jakarta. Industrial and Systems Engineering Assessment Journal (INASEA), 9(2).

Mulyani, S. 2006. Stabilisasi Tanah Lempung Dengan Emnggunakan Abu Terbang Dan Kapur (Doctoral dissertation, Universitas Gadjah Mada).

Munir, Misbachul . 2008 . Pemanfaatan Abu Batubara (fly Ash) untuk Hollow Block yang Bermutu dan Aman bagi Lingkungan. Semarang : Universitas Diponegoro.

Presiden RI. 1997. Undang Undang No. 32 Tahun 2009 Tentang : Pengelolaan Lingkungan Hidup. Kemmentrian Hukum dan Ham RI : Jakarta.

Sastrosupardi, Adji. 1999. Rancangan Percobaan Praktis Bidang Pertanian, edisi Revisi. Kanisius, Malang.

Sebayang, Surya. 2010. Pengaruh Kdar Abu Terbang sebagai pengganti sejumlah Semen pada Beton Alir Mutu Tinggi. Bandar Lampung :Universitas Lampung.

SNI-03-0691-1996, Persyaratan mutu bata beton (paving block),. Badan Standarisasi Nasional, Jakarta.

Suseno, Hendro. 2012 . Pengaruh Penggunaan Bottom Ash Sebagai Pengganti Tanah Liat pada Campuran Bata Terhadap Kuat Tekan Bata. Universitas Brawijaya, Malang.

Yusuf, Yulizar .2013. Pengaruh Penambahan Abu Terbang (Fly Ash) Terhadap Kuat Tekan Mortar Semen Tipe PCC Serta Analisis Air Laut Yang Digunakan Untuk Perendaman. Jurusan Kimia, Fakultas MIPA, Universitas Andalas : Padang.

Zakaria, 2003, Analisis Kandungan Mineral Magnetik pada Batuan Beku dari Daerah Istemewa Yogyakarta dengan Metode X-Ray Diffraction, skripsi, Fakultas Keguruan dan Ilmu Pendidikan, Universitas Halouleo, Kendari.




DOI: https://doi.org/10.30736/jt.v11i1.288

Refbacks

  • Saat ini tidak ada refbacks.